Lugar de origem
Henan, China
Material
Natural bauxite , calcium aluminate
Refractoriness (grau)
1770°< Refratividade< 2000°
Número do Modelo
high alumina cement
Serviço de processamento
Flexão, Soldagem, Perfuração, Decoiling, Corte, Moldagem
Rupture strength MPa(1days)
4.0-5.5
Rupture strength MPa(3 days)
5.0-6.5
Cold crushing strength (Mpa)
≥65
Rupture strength MPa (28 days)
10.0
Compressive strength MPa (1 days)
20-40
Compressive strength MPa (3 days)
30-50
Compressive strength MPa (28 days)
80
Setting time Min
lnitial time ≥30 Final time ≤360